Statistical properties of microcracking in polyurethane foams under tensile test, influence of temperature and density

Abstract

We report tensile failure experiments on polyurethane (PU) foams. Experiments have been performed by imposing a constant strain rate. We work on heterogeneous materials for whom the failure does not occur suddenly and can develop as a multistep process through a succession of microcracks that end at pores. The acoustic energy and the waiting times between acoustic events follow power-law distributions. This remains true while the foam density is varied. However, experiments at low temperatures (PU foams more brittle) have not yielded power-laws for the waiting times. The cumulative acoustic energy has no power law divergence at the proximity of the failure point which is qualitatively in agreement with other experiments done at imposed strain. We notice a plateau in cumulative acoustic energy that seems to occur when a single crack starts to propagate.

References in corpus (6)

• Acoustic Emission from Paper Fracture
• Critical Ruptures
• Andrade and Critical Time-to-Failure Laws in Fiber-Matrix Composites: Experiments and Model
• Subcritical statistics in rupture of fibrous materials: Experiments and model
• Failure time and microcrack nucleation
• Self-Similar Law of Energy Release before Materials Fracture

Cited by in corpus (6)

• Intermittency and roughening in the failure of brittle heterogeneous materials
• Sound and light from fractures in scintillators
• Creep rupture as a non-homogeneous Poissonian process
• Interface propagation in fiber bundles: Local, mean-field and intermediate range-dependent statistics
• Damage spreading in quasi-brittle disordered solids: II. What the statistics of precursors teach us about compressive failure
• How criticality meets bifurcation in compressive failure of disordered solids