Failure mechanisms and surface roughness statistics of fractured Fontainebleau sandstone

Abstract

In an effort to investigate the link between failure mechanisms and the geometry of fractures of compacted grains materials, a detailed statistical analysis of the surfaces of fractured Fontainebleau sandstones has been achieved. The roughness of samples of different widths W is shown to be self affine with an exponent zeta=0.46 +- 0.05 over a range of length scales ranging from the grain size d up to an upper cut-off length ξ= 0.15 W. This low zeta value is in agreement with measurements on other sandstones and on sintered materials. The probability distributions P(delta z,delta h) of the variations of height over different distances delta z > d can be collapsed onto a single Gaussian distribution with a suitable normalisation and do not display multifractal features. The roughness amplitude, as characterized by the height-height correlation over fixed distances delta z, does not depend on the sample width, implying that no anomalous scaling of the type reported for other materials is present. It is suggested, in agreement with recent theoretical work, to explain these results by the occurence of brittle fracture (instead of damage failure in materials displaying a higher value of zeta = 0.8).

arXiv comment7 pages

References in corpus (10)

• Two-dimensional scaling properties of experimental fracture surfaces
• Scaling exponents for fracture surfaces in homogenous glass and glassy ceramics
• Anomalous Scaling of Fracture Surfaces
• Gaussian Statistics of Fracture Surfaces
• Anomalous roughening of wood fractured surfaces
• Low self-affine exponents of fracture surfaces of glass ceramics
• Roughening of Fracture Surfaces: the Role of Plastic Deformations
• Fracture Surfaces as Multiscaling Graphs
• Morphology of two dimensional fracture surface
• Fracture surfaces of heterogeneous materials: a 2D solvable model

Cited by in corpus (11)

• Intermittency and roughening in the failure of brittle heterogeneous materials
• Turbulent fracture surfaces: A footprint of damage percolation?
• Finite size effects on crack front pinning at heterogeneous planar interfaces: Experimental, finite elements and perturbation approaches
• Propagation of a plane-strain hydraulic fracture accounting for a rough cohesive zone
• Hydraulic transmissivity and heat exchange efficiency of open fractures: a model based on lowpass filtered apertures
• Effect of the porosity on the fracture surface roughness of sintered materials: From anisotropic to isotropic self-affine scaling
• Stability and roughness of tensile cracks in disordered materials
• Graph theoretical approaches for the characterization of damage in hierarchical materials
• Effect of Disorder and Notches on Crack Roughness
• Brittle Crack Roughness in Three-Dimensional Beam Lattices
• Implications of Realistic Fracture Criteria on Crack Morphology